Ferrite Materials

Ni-Zn Ferrite Materials for Suppression of EMI

N650

Ni-Zn type

SymbolatValueUnit
Initial permeabilityμi650 ±20%-
Flux densityBs10 kHz, 25°C
100 kHz, 25°C
350
330
mT (1600A/m)
RemanenceBr10 kHz, 25°C150mT
Coercive forceHc10 kHz, 25°C35A/m
Relative loss factortanδ/μi10 kHz20×10-6
Curie temperatureTc10 kHz>140°C
ResistivityρDC, 25°C>105Ωm
Densityγ-4.9g/cm3

N850

Ni-Zn type

SymbolatValueUnit
Initial permeabilityμi850 ±20%
Flux densityBs10 kHz, 25°C
100 kHz, 25°C
350
330
mT (1600A/m)
RemanenceBr10 kHz, 25°C200mT
Coercive forceHc10 kHz, 25°C20A/m
Relative loss factortanδ/μi10 kHz16×10-6
Curie temperatureTc10 kHz>120°C
ResistivityρDC, 25°C>105Ωm
Densityγ4.8g/cm3

Mn-Zn Ferrite Materials for Antenna Rods with high 'Q'

M1700

Mn-Zn type

SymbolatValueUnit
Initial permeabilityμi850 ±20%
Flux densityBs10 kHz, 25°C
100 kHz, 25°C
350
330
mT (1600A/m)
RemanenceBr10 kHz, 25°C200mT
Coercive forceHc10 kHz, 25°C20A/m
Relative loss factortanδ/μi10 kHz16×10-6
Curie temperatureTc10 kHz>120°C
ResistivityρDC, 25°C>105Ωm
Densityγ4.8g/cm3

M2000

Mn-Zn type

SymbolatValueUnit
Initial permeabilityμi850 ±20%
Flux densityBs10 kHz, 25°C
100 kHz, 25°C
350
330
mT (1600A/m)
RemanenceBr10 kHz, 25°C200mT
Coercive forceHc10 kHz, 25°C20A/m
Relative loss factortanδ/μi10 kHz16×10-6
Curie temperatureTc10 kHz>120°C
ResistivityρDC, 25°C>105Ωm
Densityγ4.8g/cm3

Mn-Zn Ferrite Materials for Power Transformer Cores with low loss

M2300

Mn-Zn type

SymbolatValueUnit
Initial permeabilityμi850 ±20%
Flux densityBs10 kHz, 25°C
100 kHz, 25°C
350
330
mT (1600A/m)
RemanenceBr10 kHz, 25°C200mT
Coercive forceHc10 kHz, 25°C20A/m
Relative loss factortanδ/μi10 kHz16×10-6
Curie temperatureTc10 kHz>120°C
ResistivityρDC, 25°C>105Ωm
Densityγ4.8g/cm3

High Permeability Mn-Zn Ferrite Materials for High Inductance Values

M5000

Mn-Zn type

SymbolatValueUnit
Initial permeabilityμi850 ±20%
Flux densityBs10 kHz, 25°C
100 kHz, 25°C
350
330
mT (1600A/m)
RemanenceBr10 kHz, 25°C200mT
Coercive forceHc10 kHz, 25°C20A/m
Relative loss factortanδ/μi10 kHz16×10-6
Curie temperatureTc10 kHz>120°C
ResistivityρDC, 25°C>105Ωm
Densityγ4.8g/cm3

M7000

Mn-Zn type

SymbolatValueUnit
Initial permeabilityμi850 ±20%
Flux densityBs10 kHz, 25°C
100 kHz, 25°C
350
330
mT (1600A/m)
RemanenceBr10 kHz, 25°C200mT
Coercive forceHc10 kHz, 25°C20A/m
Relative loss factortanδ/μi10 kHz16×10-6
Curie temperatureTc10 kHz>120°C
ResistivityρDC, 25°C>105Ωm
Densityγ4.8g/cm3

M10000

Mn-Zn type

SymbolatValueUnit
Initial permeabilityμi850 ±20%
Flux densityBs10 kHz, 25°C
100 kHz, 25°C
350
330
mT (1600A/m)
RemanenceBr10 kHz, 25°C200mT
Coercive forceHc10 kHz, 25°C20A/m
Relative loss factortanδ/μi10 kHz16×10-6
Curie temperatureTc10 kHz>120°C
ResistivityρDC, 25°C>105Ωm
Densityγ4.8g/cm3